| Two-Part HS Brilliant Plus Clear Coat -LZK 769 K05 A5- |
| Two-part HS brilliant clear coat is a high-gloss, VOC
compliant high solid clear coat from the two-part acrylic
system. |
| Can be used in a number of ways |
| Good spreading properties |
| Processing in two spray applications (preferred), (1.5 spray
applications possible) |
| Suitable preliminary coatings: |
|
|
|
| Two-Part VHS Hardener -LHA 009 051 A2-/-LVM 009 051 A5- |
| Two-Part VHS Hardener, Short -LHA 009 050 A2- |
| Two-Part VHS Hardener, Long -LHA 009 052 A2-/-LHA 009 052
A3- |
| Two-Part VHS Hardener, Extra Long -LHA 009 053 A2- |
| The choice of hardener depends on the temperature and the
size of the surface. See technical application information
two-part VHS hardener. Refer to
→ Chapter „Two-Part VHS Hardener and Two-Part VHS Performance
Hardener“. |
| For elastification
→ Anchor. |
| Clear Coat Additive -LVM 007 000 A2- |
| HS Spot Thinner -LVM 006 000 A2- |
| See the HS spot thinner technical application information.
Refer to
→ Chapter „HS Spot Thinner“. |
|
|
|
| Processing time/pot life: |
| – |
Ready to spray in 75 to 90 minutes at +20 °C (68 °F) |
|
|
|
| – |
Processing viscosity 4 mm for +20 °C (68 °F), German
Industry Standardization 53211 |
|
|
|
| Processing viscosity 4 mm gravity feed spraygun “Compliant”
and “HVLP” is the mixed viscosity. |
|
|
|
| Adding 5 % Clear Coat Additive -LVM 007 000 A2- at +20 °C
(68 °F) material temperature |
 Note
| When using as a clear coat for minimal damage repairs
(clever repair procedure), 5 % Clear Coat Additive -LVM 007 000
A2- can be replaced with 5 % HS Spot Thinner -LVM 006 000 A2-. |
| The mixture for the clever repair procedure described above
should not be used on reclined surfaces. |
| – |
Use a measuring stick to mix when pouring in the thinner. |
|
|
|
| – |
Set spray nozzle (see manufacturer's information):
“Compliant” 1.2 to 1.3 mm. |
| – |
Set spray nozzle (see manufacturer's information): “HVLP”
1.2 to 1.3 mm. |
| – |
Set spray pressure (see manufacturer's information):
“Compliant” to 2.0 to 2.5 bar. |
| – |
Set atomizing pressure (see manufacturer's information):
“HVLP” 0.7 bar. |
|
|
|
| Can be applied in two spray applications with a 5 to 10
minute intermediate ventilation time. The first spray
application is applied lightly, but completely. |
| Apply 1.5 spray applications. The first half spray
application should form a thin, nearly complete film upon which
a fully-completed spray application can be applied. |
| – |
The recommended dry layer thickness is between 50 and 70 µm. |
|
|
|
| Air dry at between +18 and 22 °C (64.4° and 71.6 °F) room
temperature: |
|
|
|
| Final drying time with forced drying is a minimum of 5 to 10
minutes. |
|
|
|
| Forced drying is at between +60 and 65 °C (140° and 149 °F)
for 30 to 35 minutes. |
|
|
|
| Final drying time for IR drying is a minimum of 5 to 10
minutes. |
|
|
|
| IR dry with short-wave heater for 10 to 15 minutes |
|
|
|
| Elastification for rigid and semi-rigid plastics: |
| The base material must first be mixed with 15 % Elastic
Additive -ALZ 011 001-. |
| Mixture with two-part VHS hardeners, 3:1 with 5 % Clear Coat
Additive -LVM 007 000 A2- (drying period is lengthened). |
|
|
|
| Personal Protective Equipment: |
| Note the safety data sheets |
| Wear the personal protective equipment during application |
|
|
|
| Flashpoint: |
above +23 °C (73.4 °F) |
| VOC value: 2004/42/IIB(d)(420)420 |
The EU limit for this product
(product category IIB.b) in ready-to-use form is a maximum of 420 g/L
volatile organic compounds. The VOC-value of this product in
ready-to-use form is a maximum of 420 g/L. |
| The guaranteed shelf life is: |
| 48 months from date of manufacture for Two-Part HS Brilliant
Plus Clear Coat -LZK 769 K05 A5-. |
| 24 months from date of manufacture for Clear Coat Additive -LVM
007 000 A2-. |
| Use no later than the date indicated on the label and store
in original container at +20 °C (68 °F). |
|
|
|
Definition:
Two-Part Brilliant Clear Coat -L2K 769 K04 A5-
Edition 10/2010
Product Description
...
Definition:
Two-Part HS Performance Clear Coat -LZK 769 K06 A5-
Edition 08/2012
Product Description
...
Other materials:
Emergency Wheels
Spare Wheel Notes
If Necessary, Explain to the Customer the Information About
Tires and Refer the Customer to the Owner's Manual.
The following notes listed also apply to spare wheels that
are marked wi ...
Refrigerant, Keeping Records
Note
The laws and regulations listed below are applicable in
Germany. Different or additional laws and regulations may apply
in other countries.
Addresses in other countries can be obtained from the
relevant au ...
Aqua Premium Touch-Up System
Definition:
Touch-Up Additive For Aqua Premium -LVM 035 100 A3-
Edition 10/2012
Product Description