Volkswagen Polo Service & Repair Manual: Long-Term Underbody Protection -D 314 D36 M2-, Gray

Volkswagen Polo Service & Repair Manual / General Paint Information / Original Products / Underbody Protection / Long-Term Underbody Protection -D 314 D36 M2-, Gray

Definition:

Long-Term Underbody Protection -D 314 D36 M2-, Gray

Edition 02/2010

Product description of Long-Term Underbody Protection -D 314 D36 M2-, gray

Long-Term Underbody Protection -D 314 D36 M2- is a gray coating compound with a watery synthetic dispersion base that is sprayed with a UBS gun.

The drying time depends on the layer thickness, ambient temperature and the surrounding humidity. Good ventilation and higher temperatures quicken the drying time.

The dried film shows good adhesion to galvanized and cathodic primed steel panels, as well as painted base surfaces. Due to the high resistance to abrasion and low-temperature flexibility, the long-term underbody protection is characterized by its quality stone chip protection characteristics.

The long-term underbody protection can be quickly painted over with water-based paints.

After air drying (approximately two to three hours), the material can also be painted over with conventional painting systems (contains solvents).

The dried coat sands easily after hardening.

The long-term underbody protection is used to reestablish the original structure after a repair.

The material is only temporarily resistant to gasoline and cold cleaners.

Application

Long-Term Underbody Protection -D 314 D36 M2- is suited for repair work on the underbody, wheel housing, front and rear areas. It is used on visible components, such as on the side sill, as paintable protection against stone impact, road salt and moisture corrosion.

The material is used to reestablish different surface structures on vehicles of all types after a repair.

The long-term underbody protection is suitable for dampening the sound of luggage compartments, hoods, wheel housings, and side panels as well as covering and sealing repaired surfaces, welded joints and overlaps.

Note

Before starting to apply, it is necessary to read the safety measures and advice in the safety data sheet.

Even for products which are not required to be labeled by law, the usual safety measures must be observed for chemical emissions.

Processing

Clean the surfaces to be treated well beforehand and remove any rust.

The surfaces must be free from dirt and dust, dry and grease-free.

Surfaces which are not to be coated should be covered with paper.

Bare steel surfaces are to be primed before applying the long-term underbody protection.

The long-term underbody protection is applied from the 1 L can using the UBS spray gun. The application pressure is 4 to 5 bar.

Shake the can contents vigorously for one minute before using.

Caution

Do not spray onto the steering, engine, driveshaft, exhaust, catalytic converter and brake systems.

Blow out the spraygun immediately after use and then rinse it with Plastic Cleaner -D 195 850 A1-.

If the spray gun becomes blocked the can may burst!

Observe the operating instructions of the UBS spray gun!

Painting Over

Note

The long-term underbody protection can be painted over with water-based and solvent-containing paints. Due to the large number of available systems on the market, testing is necessary.

1 -	Painting over with water-soluble paints:

–	After a short drying period (matte surface), the long-term underbody protection can be painted over up to 72 hours after applying with water-soluble paints.

2 -	Painting over with conventional (solvent-containing) paints:

–

After drying, the long-term underbody protection can be painted over up to 72 hours after applying with conventional (solvent-containing) paints. The material has a quick-drying thick layer system. If accelerating the drying period in an airflow, then make sure that the rapidly forming film is not being actively blown onto the material that is still drying. This could lead to crack formation.

Cleaning

Splashes on painted surfaces should be removed immediately using Plastic Cleaner -D 195 850 A1-.

Equipment or the dirty parts of the equipment should be cleaned after applying water, and if necessary, adding of a watery cleaner. Do no use any solvent-containing cleaners (clotting). After drying, the long-term underbody protection can only be removed using a tool.

Technical Data

Technical Data:
Color	grey
Odor	slightly like ammonia
Density	approximately 1.22 g/cm³
Solid matter content	approximately 67 %
Viscosity:	0.5 Pas
Measuring instrument	Physica
Measuring system	Z 4
Wet application thickness	1 mm
Thinner/cleaner	distilled water
Processing temperature	+10 °C to +25 °C (50° to 77 °F)
Application temperature	-25 °C to +80 °C (-13° to 176 °F) (short-term, up to one hour at +100 °C (212 °F))
Acoustic data:
Dissipation factor DIN 53440	Approximately 0.10
Temperature	+20 °C (68 °F)
Frequency	200 Hz
Material	1 mm steel panel
Coating to panel thickness ratio	2:1

Storage

The guaranteed shelf life is 12 months from the production date. Use no later than the date indicated on the label and store in original container at +20 °C (68 °F)

Long-Term Underbody Protection -D 314 D36 M2-, Gray

Storage Conditions

The recommended storage temperature for the long-term underbody protection is +10 °C to +25 °C (50° to 77 °F)

The long-term underbody protection is vulnerable to frost. It must not fall below +5 °C (41 °F).

Long-Term Underbody Protection -D 314 D36 M2-, Gray

Underbody Protection

...

Long-Term Underbody Protection -D 314 D37 M2-, Black

Definition: Long-Term Underbody Protection -D 314 D37 M2-, Black Edition 02/2010 Product description of ...

Other materials:

Lifting the vehicle with the jack
Fig. 168 Jacking points for the vehicle jack (mirrored on the right-hand side of the vehicle) Fig. 169 Vehicle jack at the rear left-hand side of the vehicle First read and observe the introductory information and safety warnings The jack may be applied only at the jacking points shown (m ...

Factory Paint Paint Structure
Structure of a Solid-Color Paint System, Conventional Approximately 80-120 µm thick 1 - Steel Panel 2 - Zinc Phosphate Coating 3 - Electr ...

Two-Part HS Brilliant Plus Clear Coat
Definition: Two-Part HS Brilliant Plus Clear Coat -LZK 769 K05 A5- Edition 02/2012 Product Description Two-part HS brilliant clear coat is a high-gloss, VOC compliant high so ...